प्रतिबल (स्ट्रेस)

परिभाषा

बाहरी बलों के कारण किसी सामग्री के भीतर प्रति इकाई क्षेत्रफल पर आंतरिक बल, पास्कल (Pa) या PSI में मापा जाता है।

व्याख्या

A 10,000 N load spread over 0.01 m² produces 1 MPa (megapascal) of stress. Structural steel yields at around 250 MPa and fractures near 400–500 MPa. Engineers design bridges and buildings to keep stresses well below material yield points, with safety factors typically of 1.5–3x. Stress concentration at holes, notches, or cracks can multiply local stress many times above the average.

02

RELATED ARTICLES

Torque Units: Newton-Meters, Pound-Feet, and Applications

From automotive specs to bolt tightening, torque units explained — N·m, lb·ft, kgf·m, and how torque relates to power.

 Pressure Units Explained: Pascal, PSI, Bar, and ATM

A practical guide to pressure units used in weather, engineering, medicine, and diving — with conversion factors and real-world reference points.

 Density Units: kg/m³, g/cm³, and Specific Gravity

A practical guide to density units — how they relate, what common materials weigh per volume, and why objects float or sink.
03

RELATED TERMS

बलाघूर्ण (टॉर्क)

टॉर्क बल का घूर्णी समतुल्य है, लागू बल और धुरी से लंबवत दूरी का गुणनफल, न्यूटन-मीटर (N·m) या पाउंड-फुट (lb·ft) में मापा जाता है।

विकृति (स्ट्रेन)

लागू प्रतिबल के अंतर्गत किसी सामग्री की विरूपण (लंबाई में परिवर्तन) और उसकी मूल लंबाई का विमारहित अनुपात: ε = ΔL/L₀।

श्यानता (विस्कोसिटी)

द्रव का विरूपण या प्रवाह का प्रतिरोध, द्रव परतों के बीच आंतरिक घर्षण को मापता है; गतिशील श्यानता पास्कल-सेकंड (Pa·s) या सेंटीपोइज़ (cP) में मापी जाती है।

RPM

RPM (प्रति मिनट चक्कर) घूर्णन गति की इकाई है जो बताती है कि कोई वस्तु एक मिनट में कितने पूर्ण चक्कर लगाती है।

तन्य शक्ति

किसी सामग्री का अधिकतम प्रतिबल जिसे वह टूटने से पहले खिंचाव के दौरान सहन कर सकती है, मेगापास्कल (MPa) या PSI में मापा जाता है।